Compaq heat shrink wraparound sleeves are manufactured from thermally stabilized cross-linked polyolefin, with a hot melt adhesive liner on the inner side of the sleeves. Upon heating, the sleeve shrinks and the adhesive melts, creating a water tight bond between the sleeve and cable sheath or cable Joint assembly components. CRS wraparound sleeve meat & even exceed the various national & international quality standards applicable. A corrosion proof stainless steel channel is used to close the sleeve during installation.
Compaq heat shrinkable wraparound sleeves are designed to repair damaged cable sheath. It is also suitable for use for rejecting of cable Joints and as additional corrosion protection on undamaged cables.
Quick & easy to apply, it provides maximum protection against correction & waterproof.
- Provides water tight seal upon recovery
- Excellent mechanical strength
- Application procedure is quick, simple & clean
- Covered with thermochromatic paint that change colure upon achieving correct shrink temperature
- Sleeve can be cut to suit shorter application requirement on site.
- Stainless steel channel provides permanent closer system
|Product Code||Expended I.D.(Min) D1||Recovered I.D.(Max)D2||Application Range (Dia) (mm)||Recovered WallThickness (W)|
D 1 - Dimensions as supplied • D 2 - Dimension after full shrinking • W - Wall thickness after full recovery
|Tensile Strength||17 n/mm2 (Mpa)(Min)||ASTM D638/ISO 37|
|Ultimate Elogation||300 % (Min)||ASTM D 638/ISO 37|
|Longitudinal Change||10 % (Min)||ASTM D 2671|
|Water Absorption||0.2% (Max)||ASTM D570/ISO 62|
|ESCR 48 hrs. for 500C||No Crack||ASTM D570|
|Torchability||No Split||TE 201 AOL|
|Accelerated Ageing||(1200C for 500 hrs||ASTM D2671/ISO 188|
|Tensil Strength||15 N/mm2 (Mpa) (Min)||ASTM D638|
|Ultimate Elongation||220% (Min)||ASTM D638|
|Low Temperature Flexibility 4 Hours at 200 C + 30C||No Cracking||ASTM 2671|
|Temp. Including Paint Conversion 1500C for 30 min 2500C for 5 min||No change Colour Change||Visula Visula|
|Dielectric Strength||12 kV/mm||ASTM D149/IEC 60243|
|Volume Resistivity||1 x 1012 ohm cm Min||IEC 60093|
|Dielectric Constant||5 Max||IEC 60250|
|Chemical Resistance in 0.1 N|
|Sol. of Na2So4Na2NaCI2H2So4|
|Tensil Strength||15 N/mm2 (Mpa) (Min)||ASTM D6328/ISO 37||Elogation||200% (Min)||ASTM D638/ISO 37|